This metal defect is known as stress corrosion cracking. 其金属缺陷就称为应力锈蚀腐蚀裂纹。
Intergranular stress corrosion cracking behavior of austenitic steels on hydrogenated high-temperature. 奥氏体钢在高温氢化物中的晶间应力腐蚀开裂性能。
The analysis results indicated that the H_2S in the LPG caused sulfide stress corrosion cracking (SSCC) of the flange. 分析结果表明,法兰断裂是由液化气中的H2S所引起的应力腐蚀开裂。
The analysis results indicated that the H2S in the LPG caused sulfide stress corrosion cracking (SSCC) of the flange. 分析结果表明，法兰断裂是由液化气中的H2S所引起的应力腐蚀并裂。
The results show that the cracking of the pipe is a kind of stress corrosion cracking (SCC). 分析结果表明，高压油管的开裂是应力腐蚀开裂造成的。
Stress corrosion cracking occurs in both aluminum and magnesium alloys as well as steel. 铝和镁合金以及钢都会发生应力锈蚀腐蚀的破裂。
Relationship between yield strength and near-neutral pH stress corrosion cracking resistance of pipeline steels-an effect of microstructure. 管道钢的屈服强度和抗近中性pH应力腐蚀开裂间的关系-显微结构的影响。
Commonly used as stem material in pressure-rated valves, silicon bronze has greater resistance to stress corrosion cracking than common brasses. 通常用作额定压力阀门的阀杆材料的硅青铜比普通黄铜具有更好的抗应力腐蚀裂纹的性能。
The reason and the main influence factors to the stress corrosion cracking of the sphere were analysed, preventing countermessure had been proposed. 对球罐应力腐蚀开裂的原因和主要影响因素进行了分析，并提出了防止对策。
The stress corrosion cracking threshould stress intensity K_(1scc) of aluminum alloy LD10CS is measured by DCB specimen in the present paper. 本文用DCB试样测量铝合金LD10CS的应力腐蚀界限应力强度因子K_(1SCC)。
The presence of the greater resid-ual tensile stress induces the stress corrosion cracking in the course of the acid pickling. 其原因是磁屏表面存在较大的切向拉应力，从而在酸洗过程中产生了应力腐蚀开裂。
By the testing, it will be found that tempering makes the K_(1scc)(stress corrosion cracking threshold level for plane strain condition) changed. 由试验结果可知回火会使K_((?) scc)(平面应变条件下的应力腐蚀开裂门槛值)改变.
Stress corrosion cracking and fatigue corrosion cracking are easily seen in ship propeller made of copper alloy for working in seawater. 采用锰黄铜或铝青铜铸造的大型海船螺旋桨在海水中工作时容易产生应力腐蚀裂纹和腐蚀疲劳裂纹。
Commonly used as stem materials in pressure-rated ales, silicon bronze has greater resistance to stress corrosion cracking than common brasses. 通常在压力等级阀门中作为阀杆材料使用。在防止金属超压力引起的腐蚀造成的断裂方面,硅青铜比常见的黄铜具有更好的性能。
The intergranular stress corrosion cracking(SCC) problem in steel shells on hightemperature blast furnace stoves was investigated in this paper. 以高风温热风炉的沿晶应力腐蚀断裂问题为背景，研究了低合金钢在硝酸盐溶液体系中的应力腐蚀行为。
Commonly used as stem materials in pressure-rated valves, silicon bronze has greater resistance to stress corrosion cracking than common brasses. 通常在压力等级阀门中作为阀杆材料使用。在防止金属超压力引起的腐蚀造成的断裂方面,硅青铜比常见的黄铜具有更好的性能。
Stress Corrosion Cracking of polythionic acids(PSCC) of 304 SS were investigated by SSRT,SEM and metallographic analysis. 通过对隔板的检查和分析,判断隔板断裂属于连多硫酸引起的应力腐蚀开裂。
The examination and analysis reveal that the cracking of the plates is the result of stress corrosion cracking (SCC) caused by polythionic acid. 通过对隔板的检查和分析,判断隔板断裂属于连多硫酸引起的应力腐蚀开裂。
The stress corrosion cracking (SCC) behaviour of 7075 aluminum alloy was studied using slow strain rate test (SSRT) technique. 采用慢应变速率试验(SSRT)研究了7075铝合金的应力腐蚀行为。
This alloy retards stress corrosion cracking and has improved resistance to sulfuric acid. alloy 20 finds wide use in all phases of chemical processing. 这种合金能够缓解金属超应力引起的腐蚀所造成的断裂,其抗硫酸腐蚀的性能也有很大的改善。合金20在化工生产过程中具有广泛的应用。