Through metallographic examination and SEM analysis of upset cracks,the cause of the formation of surface pores of steel # 45casting blank is studied.

• 从对顶锻裂纹缺陷进行金相分析、扫描电镜分析出发,研究45%23钢铸坯表面气孔形成的原因;