The surface chemical effects of epoxy during dry friction were scission of macromolecular chains and oxidative degradation, and fatigue wear was the main wear mechanism.

• 环氧树脂在干摩擦过程中发生的表面化学效应主要是其分子链的断裂和氧化降解，其磨损形式主要为疲劳磨损。