The smallest crystal size of the anatase phase from TiO2/DEA was approximately 5 nm, and the larger particles of the rutile phase from all types of N-doped TiO2 exceeded an average of 10 nm.

• 混合钛矿和金红石相显然是目前在联合国掺杂TiO2 ， TiO2/TEN和TiO2/urea 。微晶尺寸观察TEM照片均符合这些所得估计高峰扩大X射线衍射谱。最小的晶体大小的锐钛矿相从TiO2/DEA约5纳米，大颗粒的金红石相所有类型的N -掺杂TiO2超过平均10纳米。