The pre-straining prolonged the fatigue crack initiation life, and increased resistance coefficient and equivalent stress threshold of the fatigue crack initiation.

• 预应变可以延长疲劳裂纹形成寿命，提高疲劳裂纹形成的抗力系数和裂纹形成的当量应力门槛值；