The impart sensitivity and friction sensitivity of HMX/TATB compounds with 10% TATB prepared by in-stiu rooting is 24%, 0% respectively.

• 机械感度测试结果表明，在TATB含量相当的情况下，原位包覆法样品具有更低的机械感度，在TATB含量为10%25时，撞击感度为24%25，摩擦感度为0%25。