The cracks mainly propagate at interfaces between the steel matrix and the eutectic ledeburite, and in the steel matrix and through the eutectic carbide.

• 热疲劳裂纹主要在钢基体与共晶莱氏体界面处、钢基体内扩展及穿越共晶碳化物。